Образцы стали 16Х12ВМСФБР были выдержаны в свинце с единичной активностью кислорода при 920 (900) К в течение 15 часов с последующим нанесением искусственного дефекта и повторной выдержкой при температуре 900 (940) К в течение 15 часов.

Результаты (английский) 1:

Samples of steel 16H12VMSFBR were decorated in lead with a single activity of oxygen in 920 (900) to within 3:00 pm with the subsequent drawing of artificial defect and repeated exposure at a temperature of 900 (940) to within 3:00 pm.

Результаты (английский) 2:

16H12VMSFBR steel samples were incubated in the lead with a single oxygen activity at 920 (900), K for 15 hours followed by application of the artificial defect and the re-heating at a temperature of 900 (940), K for 15 hours.

Результаты (английский) 3:

the samples were 16х12вмсфбр were conducted in the lead, with a single active oxygen in 920 (900) for 15 hours, followed by an artificial defect and re poise at a temperature of 900 (940) to within 15 hours.